S355M 1.8823 - EN 10025-4-2004

牌号	S355M
欧标钢号	1.8823
对应标准	EN 10025-4-2004 结构钢热轧产品第4部分热机械轧制可焊接细晶粒结构钢

S355M 化学元素成分含量(%)

成分	C ^*	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu ^④	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	-	-	-	-	-	-	-	-	-	-	-	0.015
最大值	0.16	0.55	1.7	0.035	0.03	0.35	0.55	0.6	0.13	0.017	0.06	0.12	0.06	-

① For long products the P and S content can be 0.005% higher.
② For railway applications a maximum S content of 0.012% may be agreed at the time of enquiry and order.
③ If sufficient other N-binding elements are present the minimum total AI content does not apply.
④ Cu content above 0.45% may cause hot shortness during hot forming.

* For long products a maximum C content of 0.17% for grade S275 and a maximum C content of 0.18% for grade S355 applies.

近似对照表结构、压力容器和工程钢

美国	德国	法国	欧标		瑞典	英国
ASTM	DIN EN/DIN	NF EN/NF	EN	数字牌号	SS	BS EN/BS
A572Gr.C A913Gr.50	StE355 StE355TM	E355 E355R	S355M FeE355KGTM①	1.8823	2134-01	50D

S355M 对应不同标准

1	EN 10025-4-2004 结构钢热轧产品第4部分热机械轧制可焊接细晶粒结构钢
	S355M 1.8823
2	EN 10025-4-2019 热机械轧制可焊接细晶粒结构钢
	S355M 1.8823

注：数据仅供参考！如有疑问，请填写"我要纠错"！