S275NL 1.0491 - EN 10025-3-2004

牌号	S275NL
欧标钢号	1.0491
对应标准	EN 10025-3-2004 热轧结构钢钢材第3部分：正火/正火轧制可焊接的细晶结构钢 Hot rolled products of structural steels - Part 3: Technical delivery conditions for normalized/normalized rolled weldable fine grain structural steels

S275NL 化学元素成分含量(%)

成分	C	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu ^④	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	0.5	-	-	-	-	-	-	-	-	-	-	0.02
最大值	0.16	0.4	1.5	0.025	0.02	0.3	0.3	0.55	0.1	0.015	0.05	0.05	0.05	-

① For long products the P and S content can be 0.005% higher.
② For railway applications a maximum S content of 0.010% may be agreed at the time of enquiry and order.
③ If sufficient other N-binding elements are present the minimum total Al content does not apply.
④ Cu content above 0.40% may cause hot shortness during hot forming.

S275NL 机械性能

公称厚度 t mm	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
t≤16	370~510	≥275	≥24
16<t≤40	370~510	≥265	≥24
40<t≤63	370~510	≥255	≥24
63<t≤80	370~510	≥245	≥23
80<t≤100	370~510	≥235	≥23
100<t≤150	350~480	≥225	≥23
150<t≤200	350~480	≥215	≥23
200<t≤250	350~480	≥205	≥23

For plate,strip and wide flats with widths≥600mm the direction transverse (t) to the rolling direction applies. For all other products the values apply for the direction parallel (l) to the rolling direction

近似对照表碳素结构钢和工程用钢

美国	德国	欧标		英国
ASTM	DIN EN/DIN	EN	数字牌号	BS EN/BS
A633Gr.A	TStE285	S275NL FeE275KTN①	1.0491	43EE

S275NL 对应不同标准

1	EN 10025-3-2004 热轧结构钢钢材第3部分：正火/正火轧制可焊接的细晶结构钢
	S275NL 1.0491
2	EN 10025-3-2019 正火/正火轧制可焊细粒结构钢
	S275NL 1.0491

注：数据仅供参考！如有疑问，请填写"我要纠错"！