S275ML 1.8819 - EN 10025-4-2019

牌号	S275ML
欧标钢号	1.8819
对应标准	EN 10025-4-2019 热机械轧制可焊接细晶粒结构钢 Technical delivery conditions for thermomechanical rolled weldable fine grain structural steels
归类	合金钢

S275ML 化学元素成分含量(%)

成分	C ^④	Si	Mn	P ^①	S ^①②	Cr	Ni	Cu	Mo	N	Ti	V	Nb	Al ^③
最小值	-	-	-	-	-	-	-	-	-	-	-	-	-	0.02
最大值	0.13	0.5	1.5	0.025	0.02	0.3	0.3	0.55	0.1	0.015	0.05	0.08	0.05	-

① For long products the P and S content can be 0.005% higher.
② For some applications, e.g. for railways, a maximum S content of 0,010 % may be agreed upon at the time of the order.
③ If sufficient other N-binding elements are present the minimum total Al content does not apply.
④ For long products a maximum C content of 0,15 % for grade S275.

碳当量计算

S275ML 机械性能

厚度 t mm	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %
t≤16	370~530	≥275	≥24
16＜t≤40	370~530	≥265	≥24
40＜t≤63	360~520	≥255	≥24
63＜t≤80	350~510	≥245	≥24
80＜t≤100	350~510	≥245	≥24
100＜t≤150	350~510	≥240	≥24

近似对照表结构、压力容器和工程钢

德国	欧标
DIN EN/DIN	EN	数字牌号
TStE275TM TStE285TM	S275ML FeE275KTTM①	1.8819

S275ML 对应不同标准

1	EN 10025-4-2004 结构钢热轧产品第4部分热机械轧制可焊接细晶粒结构钢
	S275ML 1.8819
2	EN 10025-4-2019 热机械轧制可焊接细晶粒结构钢
	S275ML 1.8819