11CrMo9-10 1.7383 - EN 10222-2-2017

牌号	11CrMo9-10
欧标钢号	1.7383
对应标准	EN 10222-2-2017 压力用途用钢制锻件第2部分具有高温特性的铁素体和马氏体钢 Steel Forgings for Pressure Purposes. Part 2:Ferritic and Martensitic Steels with Specified Elevated Temperature Properties
归类	合金钢

11CrMo9-10 化学元素成分含量(%)

成分	C	Si	Mn	P	S	Cr	Cu	Mo
最小值	0.08	-	0.4	-	-	2	-	0.9
最大值	0.15	0.5	0.8	0.02	0.01	2.5	0.25	1.1

碳当量计算

11CrMo9-10 机械性能

厚度 t mm	抗拉强度 σ_b Mpa	屈服点 σ_s Mpa	断后伸长率或延伸率 δ %	冲击吸收能量 KV2 J
t≤200	520~670	≥310	≥20	I：≥40，tr/t：≥27；I：≥60，tr/t：≥50
200＜t≤500	450~600	≥265	I：≥23，tr/t：≥21	I：≥40，tr/t：≥27；I：≥50，tr/t：≥34

① I = longitudinal to main forging directions；tr = transverse to main forging directions；t = tangential.
② Maximum room temperature for the impact test is 20 °C. By option, impact testing may be carried out at 0°C, with the condition to fulfil the impact values as stated in this table.
③ Until the yield point criteria are harmonized in the various national codes, determination of ReH may be replaced by determination of Rp0.2. In this case Rp0.2 values are 10 MPa lower for ReH values up to 355 MPa and 15 MPa lower for ReH values greater than 355 MPa.

热处理制度（仅供参考）

QT= quenched and tempered; NT= normalized and tempered. a = air; f = furnaced; o = oil; w = water or water based medium.

近似对照表锅炉和压力容器用钢板

中国	日本	国际标准组织	欧标	俄罗斯
GB	JIS	ISO	EN	GOST
12Cr2Mo1R GB/T 713.2-2008	STFA24 JIS G3467-1988	13CrMo9-10 ISO 9328-2004	11CrMo9-10 EN 10028-2003	10Х2М GOST 5520-1979

11CrMo9-10 对应不同标准

1	EN 10216-2-2007 压力无缝钢管.交货技术条件.规定高温特性的非合金和合金钢管
	11CrMo9-10 1.7383
2	EN 10273-2000 有特定高温性能的压力装置用热轧可焊接钢棒
	11CrMo9-10 1.7383
3	ISO 9330-2-1997 具有特定高温性能的电阻和感应焊接非合金和合金钢管
	11CrMo9-10
4	ISO 9330-4-2000 具有特定高温性能的埋弧焊非合金和合金钢管
	11CrMo 9-10
5	EN 10222-2-2017 压力用途用钢制锻件第2部分具有高温特性的铁素体和马氏体钢
	11CrMo9-10 1.7383
6	NF EN 10216-2-2007 高温用承压无缝钢管
	11CrMo9-10 1.7383
7	EN 10028-2-1992 压力容器用钢扁平产品-第 2 部分：规定高温性能的非合金和合金钢
	11CrMo9-10 1.7383

注：数据仅供参考！如有疑问，请填写"我要纠错"！

热处理制度（仅供参考）